Aluminum carbide
The molecular formula of Al4C3 is used to describe this inorganic compound. Aluminum carbide comes as a yellow, greenish gray or white crystal block. It’s hygroscopic. Aluminum carbide powder decomposes in high temperature water and is then dissolved into aluminum hydroxide and methane.
Then, spread carbon powder over the top of a tightly packed layer of heavy smoke black, 6 parts aluminum powder and pine essential oil. Cover the crucible with a lid. Fill in all gaps with refractory dirt mixed with asbestos fibres. Then, the crucible is placed in an oven and pre-dried. After that, the mixture will be fired for 30 minutes at a temperature no lower than 1200degC.
After cooling, the product will be treated with dilute alkaline or hydrochloric acids (or diluted hydrochloric solution) to remove excess aluminium. After obtaining the aluminum carbide as a fine crystalline, powder, it is washed to remove the aluminum chloride. Alcohol is then used to quickly wash away the water. The product is then dried in a box set at a temperature between 80 and 90degC. The product contains an excessive amount of aluminum chloride.
Aluminum carbide itself is colorless. However, the products that are made using the above method can have a variety of colors because the raw materials used to make them contain impurities.
A pure product free of aluminum nitride is obtained when the calculated quantity of the mixture of aluminium and soot are calcined with hydrogen. This calcination is carried out between 1800degC and 1900degC, for a duration of 2 to3 hours. The product is ground, and then calcined once more at the mentioned temperature.
1. When combined with silicon carbide, the finely distributed aluminum carbide in the aluminum matrix reduces the tendency of material to creep.
2. The aluminum-aluminum carbide composite material can be made through mechanical alloying by grinding graphite and aluminum powder together.
3. Aluminum carbide may be used in high speed cutting tools. It is hard enough to be used in high-speed cutting tools.
4. Aluminum carbide, used as a firework additive, can be used, for instance, to produce the effect of fireflies.
Tech Co., Ltd. is a professional Aluminum carbide powder Over 12 years in research and product development. You can contact us for high quality Aluminum carbide Powder. Contact us Send an inquiry.
The preparation of aluminum carbide
Aluminum carbide is produced by heating alumina with coke in a furnace. Aluminum carbide Al4C3 comes from the direct combination of two metals at high temperature.Then, spread carbon powder over the top of a tightly packed layer of heavy smoke black, 6 parts aluminum powder and pine essential oil. Cover the crucible with a lid. Fill in all gaps with refractory dirt mixed with asbestos fibres. Then, the crucible is placed in an oven and pre-dried. After that, the mixture will be fired for 30 minutes at a temperature no lower than 1200degC.
After cooling, the product will be treated with dilute alkaline or hydrochloric acids (or diluted hydrochloric solution) to remove excess aluminium. After obtaining the aluminum carbide as a fine crystalline, powder, it is washed to remove the aluminum chloride. Alcohol is then used to quickly wash away the water. The product is then dried in a box set at a temperature between 80 and 90degC. The product contains an excessive amount of aluminum chloride.
Aluminum carbide itself is colorless. However, the products that are made using the above method can have a variety of colors because the raw materials used to make them contain impurities.
A pure product free of aluminum nitride is obtained when the calculated quantity of the mixture of aluminium and soot are calcined with hydrogen. This calcination is carried out between 1800degC and 1900degC, for a duration of 2 to3 hours. The product is ground, and then calcined once more at the mentioned temperature.
Aluminum Carbide Application
Aluminum carbide has many applications, including in the production of methane and catalysts. Other typical uses of aluminum carbide are:1. When combined with silicon carbide, the finely distributed aluminum carbide in the aluminum matrix reduces the tendency of material to creep.
2. The aluminum-aluminum carbide composite material can be made through mechanical alloying by grinding graphite and aluminum powder together.
3. Aluminum carbide may be used in high speed cutting tools. It is hard enough to be used in high-speed cutting tools.
4. Aluminum carbide, used as a firework additive, can be used, for instance, to produce the effect of fireflies.