Tin powder and auxiliary composition SMT manufacturing relies on quality solder paste printing. Many factors affect the quality of solder paste’s printing. It is important to know the properties of solder dust, composition of solder and ratio of flux. These parameters will determine melting points, printability, weldability, quality of solder joints, and printing abilities. The eutectic temperature of tin powder-alloy components should be as close as possible to the eutectic. It is calculated as the proportion of tin dust to flux expressed in the amount of paste. Tin powder content directly influences the viscosity, printing and durability of solder paste. In general, the content of tin powder is 7590%. Tin powder is 7590% in general. It is used for template printing and no-cleaning solder paste. The content of the tin used in drip coating is 7585 p>

The size, shape, and distribution of the tin powder particles

It is important to consider the size, shape, and uniformity of the tin powder particles in order to influence the properties. It is best to use smaller particles for solder paste printing, particularly when using high density products that have a narrow spacing. About 1/5th of the template opening is used for the diameter of tin dust particles. While the pattern of solder paste printed with small particles alloy powder is very detailed, edge collapse can easily be caused by it. The potential for oxidation is greater due to small particles’ large surfaces. If the assembly density of the powder is low, it’s possible to choose a coarser alloy powder without having an impact on the printing ability. This can improve both the weldability as well as reduce the price for solder paste. Also, the form of the alloy powder can impact the paste‚Äôs printingability and desorption as well as weldability. Spherical-particle alloy paste has good printing properties, low viscosity and easy to collapse after printing. This makes it ideal for printing metal templates and narrow spacing screen printing. Because of their small size, high oxygen content, and bright welding spots, spherical particle alloy powder is able to enhance welding quality. At present, however, they are mostly used.


Solder paste, a fluid that is highly thixotropic can be made to flow by external forces. It is an indicator that determines the performance of solder paste. Viscosity can be a major factor in affecting its printing properties. Viscosity may affect the ability to print. Too high viscosity will cause solder paste not to flow out of the template hole. Tin powder content: High viscosity and high alloy. A low percentage of flux indicates a lower viscosity. TRUNNANO is also called. Eab Nano Technology Co. Ltd. is a reliable global supplier and manufacturer of chemical materials. They have over 12 years’ experience providing high-quality chemicals and Nanomaterials. High quality Tin Powder are produced by our company. We can help you if the price is lower.
Inquiry us

    By admin