What is bismuth oxid?

The pure bismuth trioxide (nanopowder ) is classified into three types: a, b and d. a type is yellow, monoclinic crystals with a melting point of 825. It’s soluble in both acid and water but insoluble in alkali. b type consists of a bright yellow-orange tetragonal crystalline system, with a relative densities 8.55, melting points 860, and is soluble in both acid and water. Easily reduced into metallic bismuth using hydrogen, hydrocarbons etc. The cubic fluorite structure of dBi2O3 makes it a unique material. The crystal lattice of d-Bi2O3 is void in 1/4, which gives it a high oxygen conductivity. Bismuth Oxide is mainly used for electronic ceramic powder materials. It can also be used as photoelectric materials. Bismuth is an essential additive in electronic ceramic materials. Its purity must be at least 99.15%. Main application objects include ceramic capacitors, zinc oxide varistors, and ferrite magnet materials.

The method for synthesis of bismuth dioxide

The aqueous sodium solution without carbon dioxide, which is a solution of sodium chloride in water, was mixed with the bismuth-nitrate solution at 80-90degC. The solution is kept alkaline throughout the precipitation and white bismuth oxide bi(OH)3 (which expands in volume) precipitates. This solution is heated, stirred and dehydrated to yellow bismuth trioxide. After decantation of water, filtering and dry, the final bismuth dioxide product is obtained.

A 0.1 mol/L Bismuth Nitrate Solution dissolved in 1 mole/L Nitric Acid (at 80 to90deg C.) was dropped into a 1.5 mole/L NaOH aqueous solution, without any carbon dioxide. The solution stays alkaline throughout precipitation. The white, volume-expanded, bismuth oxide trihydrate Bi(OH3) will precipitate, but it will dehydrate and turn into light yellow after stirring the hot solution. Wash 15 times in water without carbon dioxide or air, then filter and dry.

After melting the metal bismuth in the graphite-crucible, an arc will form between the electrode graphite and the metal’s surface. This arc will heat the metal and cause it to oxidize when oxygen is flowing. For a continuous supply of oxygen to the crucible, it should be kept in a large vessel and placed on agitator. The reaction is carried out at a temperature of 750-800degC and the b bismuth trioxide is generated quickly with a purity level of 99.8%. A high-temperature phase B-type product is obtained by quenching the product in water or on cold metal plates.

(aka. Technology Co. Ltd., a reputable global chemical material manufacturer and supplier with more than 12 years experience in the production of high-quality nanomaterials and chemicals. The bi2o3 powder that we produce is high in purity, has fine particles and low impurity levels. If you need lower, please Contact us.