Silicon monoxide can be described as an inorganic compound. Its chemical formula is SiO. At room temperature, it’s a brownish to darkly colored amorphous powder.
Particle Size 2um
About Silicon Monoxide, Lithium Anode Material SiO Powder
Silica monoxide can be described as an inorganic compound. The chemical formula is SiO. Under normal conditions, it has a density of 2.13g/cm 3. It dissolves in dilute hydrofluoric acids and nitric. This will release silicon tetrafluoride. Silica monoxide can oxidize to silicon dioxide when exposed to air. Slowly condensing silicon monoxide, the vapors become disproportionate (see disproportionation reactions) and form silicon and silicon dioxide.
Silica monoxide is the formula SiO and it’s insoluble in water. Si-O’s bond length is approximately 150.7pm. SiO, a yellowish-brown material in vacuum at 1800 is called. Silica monoxide can be unstable and oxidizes to silica in the air. The stable temperature for Silica Monoxide is 1200 ° C.
Hydrofluoric acid is used to dissolve silicon monoxide. Nitric acid is then used to give off silicon tetrafluoride. Silica monoxide can be dissolved in a mixture of hydrofluoric acid and nitric acid. It is an effective insulator and conductor of heat and electricity. The silica oxide forms a thin film in the atmosphere. It is then passivated. It reacts with oxygen to produce hydrogen. In a warm solution alkaline water, hydrogen gas can be produced. Send an inquiry for the latest Silicon Monoxide prices at any moment.
Performance Anode Material Silicon Monoxide siO Powder:
Silicon monoxide is chemically defined as SiO at CAS 10097-28-6. It has the formula SiO and is an amorphous, black-brownish to brownish-colored powder at room temperature. Silicon monoxide can be unstable and will oxidize in the atmosphere ..
.
Technical Parameter for Anode Material Silicon Monoxide siO Powder:
Product name
Particle Size
( D50 )
TAP
SSA
Moisture Content
Discharge Specific Capacity
Silicon Monoxide
2um
0.91 g/cc
4.7 m2/g
0.1%
1650 mAH/g
How isSilicon Monoxide Silo PowderCreated?
1. Silica can be used to make silicon monoxide. After rapid cooling, silica can also react with elemental silicon.
SiO2 + Si → 2SiO
2. SiO2 Content of 99.5% SiO2 Powder and Coal Asphalt Powder Mixed, C/SiO2 Mixed molar Ratio is 2.0. Vacuum Heating is used. At 1600 degrees Celsius, there is an argon gas reduction reaction that results in SiO vapor condensation transport. Preparation of silicon monoxide powder lower than 0.1 m.
SiO2+C→SiO+CO
Anode Material Silicon Monoxide Silo Powder
Silicon monoxide can also be used to produce fine ceramics, including silicon nitride or silicon carbide fine powder.
For the manufacture of optical glass, and other semiconductor materials, Silicon Monoxide can be used.
To protect the film, silicon monoxide must be evaporated in vacuum.
It is also possible to use silicon monoxide in the production of semiconductor materials.
In optical applications, such as reflectors or floodlights, mirrors or jewelry, the use of silicon oxide coatings is common.
SiO coatings can decrease reflection and act as interference layers in the near-infrared spectrum.
Sio also lends itself well to reflective coatings made with ZnS, and other materials.
Storage condition of anode material Silicon Monoxide SiO powder :
a. The SiO2 powder of silicon monoxide should be kept dry and well ventilated.
b. The stacking of silicon monoxide SiO should be clean and neat. It should also clearly identify the production batch number and production date.
Carefully transport the silicon monoxide SiO (silicon monoxide) powder.
Shipping and Packing of Anode Material SiO Powder & Silicon Monoxide SiO Oxide :
Many types of packing exist, which are determined by the amount silicon monoxide siO powder.
Silicon monoxide SiO Powder Packaging: 1kg/bag, 5kg/bag and 25kg/carton. Or as requested.
Shipping Silicon monoxide SiO Powder: can be shipped by sea, air or express, once the payment has been received.